Alwmina wedi'i Galchynnu ac Anhydrin

Sufficient fine grinding of the α-Al2O3 aggregates can destroy their aggregated state and make them non-porous primary crystals, at which time the particle size means close to its grain size. Activated alumina is calcined alumina that has been sufficiently finely ground and has α-Al2O3 with an original crystal size of less than 1 μm as the basic composition (20% to >9{ {12}} y cant ). Wrth gynhyrchu alwmina wedi'i actifadu, mae angen malu cryf fel arfer, fel malu sych mewn melin bêl wedi'i leinio â cherameg gyda pheli ceramig fel y cyfrwng malu am fwy na 24 awr. Mae'r rheswm pam y'i gelwir yn alwmina wedi'i actifadu fel arfer yn golygu ei bod hi'n hawdd cyflawni'r dwysedd sintro uchaf pan gaiff ei sintro, ond mae'r tymheredd sintering 100-200 gradd yn is na thymheredd y powdr gweithgaredd isel -Al2O3; Mae'n hawdd adweithio a sinter â chydrannau eraill yn y matrics deunydd, megis cyfuno â chlai yn y matrics i ffurfio mullite, adweithio â sment aluminate calsiwm i ffurfio CA6, adweithio gyda MgO i ffurfio spinel, ac ati Yn ôl y theori sintering , mae'r maint grawn yn effeithio'n fawr ar y gyfradd sintering yn y cam cychwynnol, hynny yw, ffurfio a thwf y gwddf rhwng y grawn. Os yw maint y grawn yn cael ei leihau i 1/10 o'r maint gwreiddiol (ee o 5 μm i 0.5 μm), bydd sintering 1000 gwaith i 10000 gwaith yn haws. Mae hyn yn esbonio gweithgaredd thermol uchel alwmina actifedig.

Mae'r broses malu yn defnyddio llawer o egni, felly po fwyaf mân yw'r powdr, y mwyaf costus ydyw. Mae ymddangosiad micro silicon (y SiO2 niwlog a gynhyrchir wrth gynhyrchu carbid silicon neu fetel silicon) wedi cyfrannu'n fawr at ddatblygiad castables lleithder isel, sment isel a sment uwch-isel, ond mae'r SiO2 gweithredol hwn hefyd yn cyfyngu ar y castables. Tymheredd gweithredu. Os nad oes datblygiad llwyddiannus o alwmina actifedig, ni all y diwydiant castable gwrthsafol modern ddatblygu mor gyflym, ac ni fydd y tymheredd gweithredu yn fwy na 1600 gradd.

 Generally speaking, powders can be divided into two categories according to the shape of particle size distribution (PSD for short): one type has a unimodal PSD, that is, the particle size distribution curve only surrounds a special particle size (close to but not necessarily Yes D50) peak: the other type is the PSD with multi-peak, that is, there are two or more distribution peaks on the PSD curve. Whether it is unimodal or bimodal, generally the wider the PSD range, the greater the powder bulk density or green body density. The PSD powder with unimodal and narrow range has the lowest bulk density. Of course, activated alumina also has the above two types. The unimodal activated alumina is characterized by a higher percentage (>80 y cant ) o ronynnau<1μm (≈primary="" crystal="" size),="" and="" thus="" has="" a="" higher="" activity,="" and="" the="" average="" value="" of="" their="" particle="" size="" (≈grain="" size)="" is="" 0.30.="" around="" 5μm.="" the="" density="" of="" this="" activated="" alumina="" green="" body="" is="" low,="" usually="" only="" 54%="" 55%="" of="" the="" theoretical="" density="" of="" α-al2o3="" (3.98g/cm3),="" but="" its="" density="" after="" firing="" at="" 15001600="" ℃="" can="" reach="" 98%="" of="" the="" theoretical="" density,="" or="" even="" higher.="" unimodal="" activated="" alumina="" is="" easily="" and="" completely="" dispersed="" in="" water="" with="" the="" aid="" of="" dispersants="" such="" as="" sodium="" polyphosphate.="" the="" content="" of="" active="" particles="" smaller="" than="" 1="" μm="" in="" the="" multi-bee="" activated="" alumina="" varies="" greatly.="" usually="" between="" 20%="" and="" 7o%.="" the="" ratio="" of="" the="" number="" of="" active="" particles="" to="" the="" number="" of="" larger="" particles="" (="">1 μm) yn pennu ei allu a'i weithgaredd llenwi gwagle. Ar gyfer alwmina wedi'i actifadu amlfodd, dim ond ei fanylder y gall y diamedr canolrif D50 ei gynrychioli, yn hytrach na pharamedr sy'n nodweddu ei briodweddau. Gall dwysedd gwyrdd alwmina actifedig amlfodd fel arfer gyrraedd 62 y cant 68 y cant o'r gwerth damcaniaethol, sy'n amlwg yn uwch na gwerth alwmina wedi'i actifadu unimodal. Mae'r dwysedd sintered y gall alwmina actifedig amlfodd ei gyflawni yn dibynnu ar ei weithgaredd. Pan ddefnyddir yr alwmina amlfodd gweithgaredd uwch ar gyfer gwasgu a sintro, er bod ei dymheredd sintro 100-150 gradd yn uwch na thymheredd yr alwmina wedi'i actifadu unimodal llawn dwys, dim ond 94 y cant a 96 y cant o'r gwerth damcaniaethol yw ei ddwysedd sintered. Mae'r gronynnau'n hawdd eu gwahanu oddi wrth y gronynnau mwy, felly mae'r alwmina wedi'i actifadu amlfodd yn hawdd i'w wasgaru mewn dŵr. Mae ystod eang PSD yr alwmina actifedig amlfodd yn galluogi llenwi'r micropowdwr -Al2O3 i'r bylchau rhwng agregau'r brics anhydrin a'r castables a'r bylchau sy'n weddill rhwng y gronynnau powdr mawr. Felly, pan gaiff ei ddefnyddio mewn castables, er mwyn cyflawni'r un hylifedd, gellir lleihau faint o ddŵr a ychwanegir 4 y cant a 5 y cant. Ym matrics y castable, mae'r alwmina wedi'i actifadu amlfodd yn gweithredu fel iraid rhwng y gronynnau mawr, a all leihau llacio'r castable, hyd yn oed pan fydd yn destun cymysgu neu bwmpio dwys. cadw ar wahân i'ch gilydd.